特性/ Features

耐CAF性能

Anti-CAF capability

Dicy Cure,优秀的剥离强度

Dicy Cure,Excellent peel strength

优异耐热性 Td=358℃ T228=30min

Excellent thermal resistance Td=358℃ T228=30min

低Z轴热膨胀系数 Low Z-CTE 3.5%

 

应用领域/ Applications 

手机、电脑、通讯设备、仪器仪表、摄像机、电视机等。

Mobile phone, computer, communication equipment , instrumentation, VCR, television, etc.

 

主要特性 / General properties

检测项目

Item

单位

Unit

检测条件

Test Condition

规范值

Spec

典型值

Typical Value

玻璃化转变温度/Tg

DSC

150±5

150.2

剥离强度/1oz Peel Strength

N/mm

288℃, 10S

≥1.05

1.52

热应力/Thermal stress

S

288℃,solder dip

10

180 s

No delamination

弯曲强度/Flexural Strength

N/mm2

经向 LW

≥415

580

纬向CW

≥345

475

燃烧性/Flammability

E 24/125

UL94V-0

V-0

表面电阻/Surface Resistivity

After moisture

≥1.0×104

5.21×107

体积电阻/Volume Resistivity

MΩ·cm

After moisture

≥1.0×106

5.10×108

介电常数/Dielectric Constant

1 MHZ

C 24/23/50

≤5.4

4.6

介质损耗角正切/Loss Tangent

1 MHZ

C 24/23/50

≤0.035

0.015

耐电弧Arc Resistance

S

 D48/50D0.5/23

≥60

120

击穿电压/Dielectric Breakdown 

KV

 D48/50D0.5/23

≥40

57

吸水率/Moisture Absorption

%

D24/23

≤0.35

0.16

热分解温度/Td

Weight Loss 5%

≥325

358

T288(不覆铜)

min

TMA

≥5

30

Z-CTE/50-260℃

%

TMA

≤4.0

3.5

相比漏电起痕指数/CTI

V

IEC-60112

175250

200

卤素含量

Halogen

content

Cl

ppm

EDX-GP

≤900

310

Br

ppm

≤900

30

Cl+Br

ppm

≤1500

340

Specimen Thickness : 1.6mm ;    Specification sheetIPC-4101D/127is for your reference only

Explanation: C: Humidity conditioning;  D: Immersion conditioning in distilled water;  E: Temperature conditioning ;

半固化片介绍-H150HF -葡京国际注册-欢迎您PP/ Prepreg instruction

H150HF -葡京国际注册-欢迎您 PP UV Prepreg):

Prepreg Type

Resin Content(%)

压合厚度Cured thickness(mm/mil)

R/C(%)含量

公差Tolerance

Nominal

Range(±)mil

%

±

mm

mil

mm

mil

7628HRC

52

2

0.227

8.93

0.023

0.9

50

2

0.217

8.41

0.022

0.8

48

2

0.206

8.11

0.021

0.8

7628

45

2

0.192

7.56

0.019

0.8

43

2

0.183

7.20

0.018

0.7

1506

50

0

0.168

6.61

0.017

0.7

48

2

0.162

6.38

0.016

0.6

2116

59

2

0.135

5.31

0.014

0.5

57

2

0.130

5.12

0.013

0.5

55

2

0.123

4.84

0.012

0.5

53

2

0.117

4.61

0.011

0.5

1080

68

2

0.084

3.31

0.008

0.3

65

2

0.076

2.99

0.008

0.3

63

2

0.071

2.80

0.007

0.3

106

74

2

0.056

2.20

0.006

0.2

72

2

0.051

2.00

0.005

0.2

 